Aimed at zinc ingots molds,the thermal and stress fields coupling analysis was utilized to analyze the effect law of casting process and casting mould configuration on temperature field and stress field of molds and casting,thus,the cause of hot cracking in the casting mould was analyzed.
以锌锭铸模为对象,采用热力耦合有限元方法,分析了浇注过程铸模及铸件温度场、应力场的变化规律,并由此剖析了铸模热裂失效产生的原因。
Failure Mechanism Research and Structure Improvement of Zinc Ingots Molds Based on ProCAST
基于ProCAST的锌锭铸模失效机制研究及结构改进
Zinc alloy ingots for casting
GB/T8738-1988铸造锌合金锭
ingot mould of metal for use in metal
金属铸造金属铸锭模
The moulds are made of cast iron.
钢锭模是用铸铁做的。
A mold in which such metal is cast.
金属铸模金属锭在其中被铸的模子
Stress-strain Analysis of Zinc Ingot Die Based on Numerical Simulation
基于数值模拟的锌锭模应力应变分析
Study on XZJ-10 New Type of Automated Zinc Ingot Stow Machine
XZJ-10新型全自动锌及锌合金锭连续铸造机组的研制
Improvement on the de-moulding mechanism for 20 kg aluminium ingot continuously casting machines
20kg铝锭连续铸造机组脱模机构的改进
Quantity and Influences in the Casting Lies the First Area of Cooling and Crystallize in Common Mold
普通模铸造一次冷却结晶区的铸锭质量及影响
Microstructure and Solidification Simulation of Φ480 ZK60 Mg Alloys Cast Ingot;
工业态Φ480ZK60镁合金铸锭组织研究及凝固模拟
Coupled Numerical Simulation of Solidification Transport Behaviours in Electromagnetic Continuous Casting of Steel Ingots;
电磁场下钢锭连铸凝固传输行为耦合数值模拟
Research on the Thermal Fatigue Property of the Aluminum Ingot Mould Material for Continuous Casting Machine Application
铝锭连铸机用模具材料热疲劳性能的研究
Impact and Improvement Measures of Tooling Mold in Remelting Aluminum Ingot Production
工装铸模对重熔用铝锭生产的影响及改进措施
The Comparative Advantages of Ingot Casting Production During the Special Steels and Large Steel Ingot Production
模铸在大钢锭及特殊钢生产方面的比较优势
Casting Process Design and Production of Aluminum Ingot Mold Export to the United States
出口美国铝锭模的工艺设计及铸造生产
The Choice of Heat Treatment Process of Ductile Iron Mould for Al Ingot
球墨铸铁铝锭模具材料热处理工艺的选择
Investigation on Thermal Stress Distribution of Cr5 Large-scale Alloy Steel Ingot by Simulating
Cr5大型合金钢铸锭热应力状态的模拟分析
In the case of rimming steel, no or some deoxidation is carried out before casting. During the solidification in the mould carbon monoxide is formed and the gas makes the steel boils.
沸腾钢在铸锭前不脱氧或轻度脱氧。在锭模中凝固的过程中产生的一氧化碳气体使钢液沸腾。