The experimental results showed that under the conditions with the ratio of the water-quenched slag and rectorite of 1∶1,the amount of the additive(IS) of 10%,the amount of 50% water,and the roasting temperature of 400 ℃,the spallation loss ratio of granulated composite material prepared was 0.
结果表明:水淬渣与累托石的比例为1∶1,另加入10%的添加剂(IS)和50%的水,焙烧温度为400℃,制成的复合颗粒材料的散失率为0。
Factors affecting flotation of water-quenched slag from a copper smelting plant in Hubei province,such as grinding fineness,pulp density,pH value and the reagent system,were studied.
对湖北某铜冶炼厂的炼铜水淬渣(含铜1。
The optimum conditions for flotation of the water-quenched slag are as follows: natural pH,Na2S 800 g/t,mixed collecting agent 240 g/t,flotation time 6 min,percent of 74 μm particles 95% and solid content 30%.
在铜熔炼反射炉渣中铜铁赋存状态分析基础上,采用常规选矿和火法贫化工艺对反射炉水淬渣进行回收铜技术探索。
The measures of steel-making with less-slag, BOF gas recycle, slag quenching and slab hot charge are carried out in the No.
济钢第一炼钢厂通过采取少渣炼钢、煤气回收、钢渣水淬、铸坯热送等措施,达到了充分回收和利用能源、合理使用资源、降低系统能耗、减少污染物排放、实现节能、清洁生产的目的,吨钢钢铁料消耗、炼钢工序能耗、耐材消耗分别降至1082kg、1045524。
Study on Recovering Copper and Cobalt from Copper Slag by Reduction Smelting
含钴铜水淬渣还原熔炼综合回收研究
Stove-exhausting gas used to dry the water-chilled dreg from a blast furnace
利用热风炉废烟气干燥高炉水淬渣的实验研究
Recovery of Copper from Water Quenched Slag of Copper Smelting by Impoverishment at High Temperature and Flotation
高温贫化-浮选法从炼铜水淬渣中回收铜
Application of Water Granulated Slag to Dispose of Blast Furnace Gas Cleaner Effluents;
含钛高炉水淬渣在高炉煤气净化水处理中的应用
Study is made of Ga recovery process from ISP or fuming furnace granulation slag.
对鼓风炉(sp法)烟化炉水淬渣中回收镓的工艺进行了研究。
Converting drilling mud to cement slurry by using blast furnace slag
用高炉水淬矿渣将泥浆转变成水泥浆
Research on the Relationship between Self-Hardening of Baosteel's Water-QuenchedG ranulated Blast Furnace Slag and Activity
宝钢高炉水淬矿渣自身水硬性和活性的关系
Here is a study on how to energize the activation of water-granulated slag to improve the slag cement's early strength.
研究了如何激发水淬矿渣的活性以提高矿渣水泥的早期强度。
Tests on Copper Separation in Flotation from Copper Slags of a Smelting Plant
从某冶炼厂水淬铜炉渣浮选回收铜的试验研究
The Research and Making of Centrifugal Graining Equipment for Molten Steel Slag and the Simulation Study of Water Quenching Method;
液态钢渣的离心粒化设备研制及水淬法模拟研究
Research of wind-quenched granulated slag grit as a substitute of sand in concrete;
风淬钢渣砂在混凝土中替代黄砂的试验研究
Application Research on Air Quench Steel Slag as a Substitute of Sand in Roadway Concrete
风淬钢渣替代砂在道路混凝土中的应用研究
cinder block (slag cement)
矿渣（矿渣水泥）砌块
steel and iron slag cement
GB13590-1992钢渣矿渣水泥
Water Quenching and Tempering Technology Research of 1000MPa Ultra-High Strength Dual-Phase Steel;
1000MPa超高强双相钢水淬及回火工艺研究
Development and trial of mold steel slab water-jet quenching system
模具钢板坯喷水淬火系统研制与试用
Development of Water-Cooled Bainitic Steel Used in Hydraulic Shelves Pillar
液压支架活柱用水淬贝氏体钢的开发
Compound Portland Cement of Slag and Coal-dust Ash
钢渣、矿渣、粉煤灰复合硅酸盐水泥