The worn surfaces of two kinds of carbon/carbon composites after 10 time simulated braking tests of an aircraft were characterized by means of micro Raman spectroscopy and X ray diffraction.
采用显微激光喇曼光谱及 X射线衍射考察了基体分别为沥青浸渍碳 /少量气相沉积热解碳和全部气相沉积热解碳的航空刹车用碳 /碳复合材料磨损表面碳结构的变化特征 ,并分析了引起这些变化的原因 。
The surface topography and components of protective coating on the worn surface of 45# steel rings were analyzed by SEM and EDAX.
当摩擦磨损时间很短时摩擦副表面就可出现自修复膜层,但成膜过程和磨损过程同步进行,随着时间的增加,膜层的形成愈来愈稳定,直至覆盖整个金属磨损表面。
Boxcounting method is applied to compute the threedimensional fractal dimensions of the worn surfaces of Ti6Al4V and plasma source ion implanted diamondlikecarbon film thereon, making use of fractal theory and scaning electron microscopic analysis of the worn surfaces.
基于分形理论和磨损表面扫描电子显微分析,采用盒子维方法计算了磨损表面的三维分形维数。
According to the surface abrasion form of cast iron seal ring, the author proposed that composite brush plating can effectively repair and strengthen the mating surface of cast iron seal ring.
根据铸铁密封环的表面磨损形式,提出采用复合刷镀技术可有效修复和强化铸铁密封环的配合面。
An experiment using electric resistance analogic method was carried out to study the surface abrasion of the internals in circulating fluidized beds (CFB).
并以边界层的发展和分离解释了内部构件表面磨损的不均匀性现象。
The working surface abrasion and scratch of the trial die were analyzed.
以换热片拉深模具为例,进行了锌基合金作为成形模的设计制造研究,对试模中出现的工作表面磨损和拉伤现象进行了分析,提出了改进的措施,最终获得了满意的效果。
It is concluded that the wearing surfaces of elastic-metallic-plastic (EMP) composite specimens,which have been tested on MPX-2000,have fractal characteristics by measuring and calculating surface profile of EMP.
通过对完成磨损试验后的弹性金属塑料（EMP）试样表面轮廓的测量与计算，获得EMP材料的磨损表面轮廓具有分形特性。
Test results of wear surface morphology dimension characterization show that wear surface profile has statistical selfaffine dimension characters.
用结构函数法对试验所得的往复式滑动磨损表面轮廓曲线进行了分形维数的计算,计算结果表明:磨损表面轮廓具有统计自仿射分形特性。
It is very important for real-time numerical video monitor of the wear surface to find the best parameters for depicting the image of the wear surface and numeralize the relationships among them.
要想对磨损表面进行实时的数字化视频监测，找出最能表达磨损表面图像的参数并量化它们之间的关系，是至关重要的。
Analysis on residual strength after casing surface wear caused in casing drilling;
套管钻井用套管外表面磨损后剩余强度分析
abraded surface
磨损表面清理过的表面
Study of Surface Characteristics Both of Wear Particles & Wear Components and Their Relationship in Wear Process;
磨损过程中的磨粒表面和磨损表面特征及其相互关系研究
Research on Mapping Model Between Wear Debris and Worn Surfaces in Sliding Bearings
滑动轴承磨损表面与磨粒信息映射模型研究
Study on Synthetical Evaluating Methods of Running-in & Wearing Surface Quality of Marine Diesel Cylinder Liner;
船舶柴油机缸套材料磨合磨损表面质量综合评价方法的研究
a hard surface that won't scuff
不会磨损的坚硬表面
Biomimetic Geometrical Structure Surfaces with Anti-abrasion Function and Their Abrasive Wear Against Soil;
耐磨仿生几何结构表面及其土壤磨料磨损
Abrasive Particle Wear Research of Die Steel Processed to Bionic Non-smooth Surface by Laser;
仿生非光滑表面模具钢材料磨粒磨损研究
Fully guided wedge reduces wear on seating surfaces.
全导向楔板减少阀座表面的磨损。
Composite Surface Strengthening of 40CrNiMoA Steel and Property of High Speed Abrasion;
40CrNiMoA复合表面强化及高速磨损性能
The Wear Simulation of UHMWPE Based on Different Surface Texture;
基于不同表面纹理的UHMWPE磨损仿真研究
Design of Biomimetic Surfaces with Domes and Abrasive Behavior Against Water-sand Slurry;
凸包型仿生表面设计及水砂磨损行为
Effect of Grinding Induced Damage on Bending Strength of RBSiC
磨削表面损伤对RBSiC弯曲强度的影响
Analysis of Wear-failure of Surface Metallurgy Coatings and Countermeasures
表面冶金涂层的磨损失效形式与对策
Generation and Control on Surface/subsurface Damage in Advanced Ceramics Grinding
工程陶瓷磨削表面/亚表面损伤的产生及其控制
Free Abrasive Wear Behavior of hte Biomimetic Non-smooth Surfaces with Convex Domes;
凸包型仿生非光滑表面自由式磨料磨料磨损行为
The Studies on Evaluation of Ground Surface Mechanical Damage of Ceramic and Grinding Based on Crack Damage Control;
陶瓷磨削表面力学损伤评价及裂纹损伤可控磨削研究
Abrasive wear may be defined as damage to a surface by a harder material.
磨粒磨损可定义为较硬的材料以一个表面的破坏。
Study on the Grinding Abrasion of Hot Die with Bionic Non-smooth Surface;
激光仿生非光滑表面热作模具的磨料磨损性能研究